Nitride based semiconductor laser device with oxynitride protective films on facets

ABSTRACT

One facet of a nitride based semiconductor laser device is composed of a cleavage plane of (0001), and the other facet thereof is composed of a cleavage plane of (000  1 ). Thus, the one facet and the other facet are respectively a Ga polar plane and an N polar plane. A portion of the one facet and a portion of the other facet, which are positioned in an optical waveguide, constitute a pair of cavity facets. A first protective film including nitrogen as a constituent element is formed on the one facet. A second protective film including oxygen as a constituent element is formed on the other facet.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a nitride based semiconductor laser device having a nitride based semiconductor layer.

2. Description of the Background Art

In recent years, nitride-based semiconductor laser devices have been utilized as light sources for next-generation large-capacity disks and have been actively developed.

In such nitride-based semiconductor laser devices, the plane directions of main surfaces of active layers are taken as substantial (H, K, −H−K, 0) planes such as (11 20) planes or (1 100) planes, so that piezoelectric fields generated in the active layers can be reduced. As a result, it is known that the luminous efficiencies of laser light can be improved. Here, H and K, described above, are any integers, and at least one of H and K is an integer other than zero.

Furthermore, it has been known that the gains of the nitride based semiconductor laser devices can be improved by setting the (0001) planes and the (000 1) planes to pairs of cavity facets (see, for example, JP 8-213692 A and Japanese Journal of Applied Physics Vol. 46, No. 9, 2007, pp.L187˜L189).

In the above-mentioned nitride based semiconductor laser devices, however, the luminous efficiency of the laser light cannot be sufficiently improved.

SUMMARY OF THE INVENTION

According to an aspect of the present invention, a nitride based semiconductor laser device includes a nitride based semiconductor layer having an optical waveguide extending in a substantial [0001] direction and having one facet composed of a substantial (0001) plane and the other facet composed of a substantial (000 1) plane as a pair of cavity facets, a first protective film provided on the one facet and including nitrogen as a constituent element, and a second protective film provided on the other facet and including oxygen as a constituent element.

The intensity of the laser light emitted from the one facet may be higher than the intensity of the laser light emitted from the other facet.

Each of a portion of the one facet and a portion of the other facet in the optical waveguide may have unevenness and the depth of a first recess in the one facet may be smaller than the depth of a second recess in the other facet.

The intensity of the laser light emitted from the other facet may be higher than the intensity of the laser light emitted from the one facet.

The first protective film may include no oxygen as a constituent element. Alternatively, the first protective film may further include oxygen as a constituent element, and the nitrogen composition ratio may be higher than the oxygen composition ratio.

The second protective film may include no nitrogen as a constituent element. Alternatively, the second protective film may further include nitrogen as a constituent element, and the oxygen composition ratio may be higher than the nitrogen composition ratio.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the one facet and including the first protective film, in which the dielectric multilayer film may include a nitride film and an oxide film that are laminated in this order from the one facet, and the first protective film may be the nitride film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the one facet and including the first protective film, in which the dielectric multilayer film may include an oxynitride film and an oxide film that are laminated in this order from the one facet, the nitrogen composition ratio may be higher than the oxygen composition ratio in the oxynitride film, and the first protective film may be the oxynitride film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the one facet and including the first protective film, in which the dielectric multilayer film may include a nitride film, an oxynitride film, and an oxide film that are laminated in this order from the one facet, the nitrogen composition ratio may be higher than the oxygen composition ratio in the oxynitride film, and the first protective film may be the nitride film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the one facet and including the first protective film, in which the dielectric multilayer film may include a first oxynitride film, a second oxynitride film, and an oxide film that are laminated in this order from the one facet, the nitrogen composition ratio may be higher than the oxygen composition ratio in the first oxynitride film, the oxygen composition ratio may be higher than the nitrogen composition ratio in the second oxynitride film, and the first protective film may be the first oxynitride film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the other facet and including the second protective film, in which the dielectric multilayer film may include a first oxide film, a nitride film, and a second oxide film that are laminated in this order from the other facet, and the second protective film may be the first oxide film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the other facet and including the second protective film, in which the dielectric multilayer film may include an oxynitride film and an oxide film that are laminated in this order from the other facet, the oxygen composition ratio may be higher than the nitrogen composition ratio in the oxynitride film, and the second protective film may be the oxynitride film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the other facet and including the second protective film, in which the dielectric multilayer film may include a first oxide film, an oxynitride film, and a second oxide film that are laminated in this order from the other facet, the nitrogen composition ratio may be higher than the oxygen composition ratio in the oxynitride film, and the second protective film may be the first oxide film.

The nitride based semiconductor laser device may further include a dielectric multilayer film formed on the other facet and including the second protective film, in which the dielectric multilayer film may include a first oxynitride film, a second oxynitride film, and an oxide film that are laminated in this order from the other facet, the oxygen composition ratio may be higher than the nitrogen composition ratio in the first oxynitride film, the nitrogen composition ratio is higher than the oxygen composition ratio in the second oxynitride film, and the second protective film may be the first oxynitride film.

The first protective film may include at least one of AlN and Si₃N₄.

The first protective film may include at least one of AlO_(X)N_(Y), SiO_(X)N_(Y) and TaO_(X)N_(Y), where X<Y.

The second protective film may include at least one of AlO_(X)N_(Y), SiO_(X)N_(Y) and TaO_(X)N_(Y), where X>Y.

The second protective film may include at least one of Al₂O₃, SiO₂, ZrO₂, Ta₂O₅, HfO₂, and AlSiO_(X), where X is a real number larger than zero.

Other features, elements, characteristics, and advantages of the present invention will become more apparent from the following description of preferred embodiments of the present invention with reference to the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a vertical sectional view of a nitride based semiconductor laser device according to a first embodiment;

FIG. 2 is a vertical sectional view of a nitride based semiconductor laser device according to a first embodiment;

FIG. 3 is a partially enlarged sectional view of the nitride based semiconductor laser device shown in FIG. 2;

FIG. 4 is a partially enlarged sectional view of the nitride based semiconductor laser device shown in FIG. 2;

FIG. 5 is a vertical sectional view of a nitride based semiconductor laser device according to a second embodiment;

FIG. 6 is a vertical sectional view of a nitride based semiconductor laser device according to a third embodiment;

FIG. 7 is a vertical sectional view of a nitride based semiconductor laser device according to a fourth embodiment;

FIG. 8 is a vertical sectional view of a nitride based semiconductor laser device according to a fifth embodiment;

FIG. 9 is a vertical sectional view of a nitride based semiconductor laser device according to a sixth embodiment;

FIG. 10 is a vertical sectional view of a nitride based semiconductor laser device according to a seventh embodiment; and

FIG. 11 is a vertical sectional view of a nitride based semiconductor laser device according to an eighth embodiment.

DESCRIPTION OF THE PREFERRED EMBODIMENTS 1. First Embodiment

(1) Configuration of Nitride Based Semiconductor Laser Device

FIGS. 1 and 2 are vertical sectional views of a nitride based semiconductor laser device according to a first embodiment. A line A1-A1 shown in FIG. 1 represents a position in longitudinal section, and a line A2-A2 shown in FIG. 2 represents a position in longitudinal section.

As shown in FIGS. 1 and 2, a nitride based semiconductor laser device 1 according to the present embodiment includes an n-type GaN substrate 101 having a thickness of approximately 100 μm in which Si (silicon) has been doped. The carrier concentration of the substrate 101 is approximately 5×10¹⁸cm⁻³.

The substrate 101 is an off substrate having a crystal growth plane inclined at approximately 0.3 degrees in a [000 1]direction from a (11 20) plane. As shown in FIG. 1, a pair of steps ST extending in a [0001] direction is formed on an upper surface of the substrate 101. The pair of steps ST is positioned on both sides of the substrate 101. The depth of each of the steps ST is approximately 0.5 μm, and the width thereof is approximately 20 μm.

An n-type layer 102 having a thickness of approximately 100 nm in which Si has been doped is formed on the upper surface of the substrate 101. Then-type layer 102 is composed of n-type GaN, and the amount of doping of Si into the n-type layer 102 is approximately 5×10¹⁸ cm⁻³.

An n-type cladding layer 103 composed of n-type Al_(0.07)Ga_(0.93)N having a thickness of approximately 400 nm in which Si has been doped is formed on the n-type layer 102. The amount of doping of Si into the n-type cladding layer 103 is approximately 5 ×10¹⁸ cm⁻³, and the carrier concentration of the n-type cladding layer 103 is approximately 5×10¹⁸ cm⁻³.

An n-type carrier blocking layer 104 composed of n-type Al_(0.16)Ga_(0.84)N having a thickness of approximately 5 nm in which Si has been doped is formed on the n-type cladding layer 103. The amount of doping of Si into the n-type carrier blocking layer 104 is approximately 5×10¹⁸ cm⁻³, and the carrier concentration of the n-type carrier blocking layer 104 is approximately 5×10¹⁸ cm⁻³.

An n-type optical guide layer 105 composed of n-type GaN having a thickness of approximately 100 nm in which Si has been doped is formed on the n-type carrier blocking layer 104. The amount of doping of Si into the n-type optical guide layer 105 is approximately 5×10¹⁸ cm⁻³, and the carrier concentration of the n-type optical guide layer 105 is approximately 5×10¹⁸cm⁻³.

An active layer 106 is formed on the n-type optical guide layer 105. The active layer 106 has an MQW (Multi-QuantumWell) structure in which four barrier layers 106 a (see FIG. 3, described later) composed of undoped In_(0.02)Ga_(0.98)N having a thickness of approximately 20 nm and three well layers 106 b (see FIG. 3, described later) composed of undoped In_(0.6)Ga_(0.4)N having a thickness of approximately 3 nm are alternately laminated.

A P-type optical guide layer 107 composed of p-type GaN having a thickness of approximately 100 nm in which Mg (magnesium) has been doped is formed on the active layer 106. The amount of doping of Mg into the p-type optical guide layer 107 is approximately 4×10¹⁹ cm⁻³, and the carrier concentration of the p-type optical guide layer 107 is approximately 5×10¹⁷cm⁻³.

An n-type cap layer 108 composed of p-type Al_(0.16)Ga_(0.84)N having a thickness of approximately 20 nm in which Mg has been doped is formed on the p-type optical guide layer 107. The amount of doping of Mg into the p-type cap layer 108 is approximately 4×10¹⁹ cm⁻³, and the carrier concentration of the p-type cap layer 108 is approximately 5×10¹⁷ cm⁻³.

A p-type cladding layer 109 composed of p-type Al_(0.07)Ga_(0.93)N in which Mg has been doped is formed on the p-type cap layer 108. The amount of doping of Mg into the p-type cladding layer 109 is approximately 4×10¹⁹ cm⁻³, and the carrier concentration of the p-type cap layer 108 is approximately 5×10¹⁷ cm⁻³.

Here, the p-type cladding layer 109 includes a flat portion 109 b formed on the p-type cap layer 108 and a projection 109 aextending in the [0001] direction on the center of the flat portion 109 b.

The thickness of the flat portion 109 b in the p-type cladding layer 109 is approximately 80 nm, and the height from an upper surface of the flat portion 109 b to an upper surface of the projection 109 a is approximately 320 nm. Furthermore, the width of the projection 109 a is approximately 1.75 μm.

A p-type contact layer 110 composed of p-type In_(0.02)Ga_(0.98)N having a thickness of approximately 10 nm in which Mg has been doped is formed on the projection 109 a in the p-type cladding layer 109. The amount of doping of Mg into the p-type contact layer 110 is approximately 4×10¹⁹ cm⁻³, and the carrier concentration of the p-type contact layer 110 is approximately 5×10¹⁷ cm⁻³.

The projection 109 a in the p-type cladding layer 109 and the p-type contact layer 110 constitute a ridge Ri. Thus, an optical waveguide WG along the [0001] direction is formed in a portion below the ridge Ri and including the active layer 106.

An ohmic electrode 111 is formed on the p-type contact layer 110. The ohmic electrode 111 has a structure in which Pt (platinum), Pd (palladium), and Au (gold) are laminated in this order. The thicknesses of Pt, Pd, and Au are 5 nm, 100nm, and 150 nm, respectively.

A current narrowing layer 112 composed of an insulating film having a thickness of approximately 250 nm covers the upper surface of the flat portion 109 b, an upper surface of the n-type cladding layer 103, and side surfaces of the above-mentioned layers 103 to 111. In this example, an SiO₂ (silicon oxide) film is used as an insulating film.

A pad electrode 113 is formed in respective predetermined regions of an upper surface of the ohmic electrode 111 and a side surface and an upper surface of the current narrowing layer 112. The pad electrode 113 has a structure in which Ti (titanium), Pd, and Au are laminated in this order. The thicknesses of Ti, Pd, and Au are approximately 100 nm, approximately 100 nm, and approximately 3 μm, respectively.

Furthermore, an n-side electrode 114 is formed on a back surface of the substrate 101. The n-side electrode 114 has a structure in which Al (aluminum), Pt, and Au are laminated in this order. The thicknesses of Al, Pt, and Au are respectively 10 nm, 20 nm, and 300 nm.

The n-type cladding layer 103, the n-type carrier blocking layer 104, the n-type optical guide layer 105, the active layer 106, the p-type optical guide layer 107, the p-type cap layer 108, the p-type cladding layer 109, and the p-type contact layer 110 constitute a nitride based semiconductor layer.

Here, out of paired cavity facets of the nitride based semiconductor laser device 1, the cavity facet having the lower reflective index and the cavity facet having the higher reflective index are respectively referred to as a light emission facet and a rear facet.

As shown in FIG. 2, a light emission facet 1F and a rear facet 1B of the nitride based semiconductor laser device 1 are respectively composed of a cleavage plane of (0001) and a cleavage plane of (000 1). Thus, the light emission facet 1F and the rear facet 1B are respectively a Ga (gallium) polar plane and an N (nitrogen) polar plane. A portion of the light emission facet IF positioned in the optical waveguide WG and a portion of the rear facet 1B positioned in the optical waveguide WG constitute a pair of cavity facets.

A first dielectric multilayer film 210 is formed on the light emission facet 1F of the nitride based semiconductor laser device 1. The first dielectric multilayer film 210 has a structure in which an AlN film 211 and an Al₂O₃ film 212 are laminated in this order. Thus, the AlN film 211 serving as a nitride film functions as a protective film of the light emission facet 1F.

The thicknesses of the AlN film 211 and the Al₂O₃ film 212 are approximately 10 nm and approximately 85 nm, respectively. The reflective index of the first dielectric multilayer film 210 is approximately 8%.

On the other hand, a second dielectric multilayer film 220 is formed on the rear facet 1B of the nitride based semiconductor laser device 1. The second dielectric multilayer film 220 has a structure in which an Al₂O₃film 221, a reflective film 222, and an AlN film 223 are laminated in this order. Thus, the Al₂O₃ film 221 serving as an oxide film functions as a protective film of the rear facet 1B.

The thickness of the Al₂O₃ film 221 is 120 nm. The reflective film 222 has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The thickness of the AlN film 223 is approximately 10 nm. The reflective index of the second dielectric multilayer film 220 is approximately 95%.

A voltage is applied between the pad electrode 113 and the n-side electrode 114 in the nitride based semiconductor laser device 1, so that laser light is respectively emitted from the light emission facet 1F and the rear facet 1B.

In the present embodiment, the first dielectric multilayer film 210 having a reflective index of approximately 8% is provided on the light emission facet 1F, and the second dielectric multilayer film 220 having a reflective index of approximately 95% is provided on the rear facet 1B, as described above. Thus, the intensity of the laser light emitted from the light emission facet 1F is significantly higher than the intensity of the laser light emitted from the rear facet 1B. That is, the light emission facet 1F is a principal emission facet of the laser light.

(2) Details of Light Emission Facet 1F and Rear Facet 1B

FIGS. 3 and 4 are partially enlarged sectional views of the nitride based semiconductor laser device 1 shown in FIG. 2. FIG. 3 is an enlarged sectional view of the light emission facet 1F and its vicinity in the optical waveguide WG, and FIG. 4 is an enlarged sectional view of the rear facet 1B and its vicinity in the optical waveguide WG.

As shown in FIGS. 3 and 4, the active layer 106 has a structure in which the four barrier layers 106 a and the three well layers 106 b are alternately laminated. In the light emission facet 1F and the rear facet 1B, the well layers 106 b in the active layer 106 project outward farther than the other layers in the nitride based semiconductor laser. Therefore, a portion of the active layer 106 in each of the light emission facet 1F and the rear facet 1B has unevenness formed by recesses and projections formed therein.

The depth D1 (FIG. 3) of the recesses of the active layer 106 in the light emission facet 1F of the nitride based semiconductor laser device 1 is approximately 1 nm, while the depth D2 (FIG. 4) of the recesses of the active layer 106 in the rear facet 1B thereof is approximately 6 nm. Note that the thinner one of the high refractive index film (TiO₂ film) and the low refractive index film (SiO₂ film), i.e., the TiO₂ film in this example, in the reflective film 222 is adjusted to a thickness larger than the depth D2 of the recesses of the active layer 106 in the rear facet 1B. In this case, the second dielectric multilayer film 220 can be easily formed so as to reliably cover the recesses and projections of the active layer 106 in the rear facet 1B. This makes it possible to ensure a high reflective index of the second dielectric multilayer film 220.

The reason why the active layer 106 has the recesses and projections formed therein is as follows. When the nitride based semiconductor laser device 1 is manufactured, the light emission facet 1F and the rear facet 1B are cleaned, as described later. In the cleaning process, the light emission facet 1F and the rear facet 1B are irradiated with ECR (Electron Cyclotron Resonance) plasma. Thus, the light emission facet 1F and the rear facet 1B are etched.

Here, the composition of the well layers 106 b in the active layer 106 differs from the respective compositions of the other layers, in the nitride based semiconductor layer, such as the barrier layers 106 a, the n-type optical guide layer 105, and the p-type optical guide layer 107. Therefore, a difference occurs between the etching amount of the well layer 106 b in the active layer 106 and the etching amount of the other layer in the nitride based semiconductor layer. Therefore, the recesses and projections are formed in the portion of the active layer 106 in each of the light emission facet 1F and the rear facet 1B.

The higher the In composition ratio ih the well layer 106 b is, the more significant the recesses and projections become. This is caused by the difference between the composition of the well layer 106 b and the composition of the other layer being greater when the In composition ratio is higher than the Ga composition ratio in the well layer 106 (0.5<x≦1). In the present embodiment, the In composition ratio x in the well layer 106 b is 0.6.

Particularly, the (000 1) plane of the nitride based semiconductor layer is chemically stabler than the (0001) plane thereof. Therefore, the difference in the etching amount between the well layer 106 b and the other layer in the (000 1) plane is greater than the difference in the etching amount between the well layer 106 b and the other layer in the (0001) plane. Thus, the depth D2 of the recesses in the rear facet 1B is larger than the depth D1 of the recesses in the light emission facet 1F.

The larger the depth of a recesses in a cavity facet having a concavo-convex shape is, the more greatly a laser light is scattered due to the concavo-convex shape. In the present embodiment, the light emission facet 1F is composed of the (0001) plane having few recesses and projections. This can inhibit the laser light from being scattered on the light emission facet 1F. As a result, a preferable far field pattern having few ripples can be obtained at the time of lasing.

(3) Method for Manufacturing Nitride Based Semiconductor Laser Device 1

A method for manufacturing the nitride based semiconductor laser device 1 having the above-mentioned configuration will be described.

First, a substrate 101 having a plurality of grooves G (see FIG. 1) extending in a [0001] direction formed on its upper surface is first prepared. The depth of the groove G is approximately 0.5 μm, and the width thereof is approximately 40 μm. A distance between the adjacent two grooves G is approximately 400 μm. Note that the groove G is previously formed in order to make the device into chips in later processes. A part of the groove G constitutes the above-mentioned step ST.

An n-type layer 102 having a thickness of approximately 100 nm, an n-type cladding layer 103 having a thickness of approximately 400 nm, an n-type carrier blocking layer 104 having a thickness of approximately 5 nm, an n-type optical guide layer 105 having a thickness of approximately 100 nm, an active layer 106 having a thickness of approximately 90 nm, a p-type optical guide layer 107 having a thickness of approximately 100 nm, a p-type cap layer 108 having a thickness of approximately 20 nm, a p-type cladding layer 109 having a thickness of approximately 400 nm, and a p-type contact layer 110 having a thickness of approximately 10 nm are sequentially formed on an upper surface of the substrate 101 by metal organic vapor phase epitaxy (MOVPE), for example.

Note that the thickness of the active layer 106 represents the total thickness of four barrier layers 106 a and three well layers 106 b.

Thereafter, annealing for changing into a p type and formation of a ridge Ri shown in FIG. 1 are performed. An ohmic electrode 111, a current narrowing layer 112, and a pad electrode 113 are formed. Furthermore, an n-side electrode 114 is formed on a back surface of the substrate 101.

Then, a cavity facet (a light emission facet 1F and a rear facet 1B) is formed, and a first dielectric multilayer film 210 and a second dielectric multilayer film 220 are formed on the cavity facet, as described later.

Scribe flaws extending in a [1 100] direction are formed in the substrate 101 on which the layers 102 to 110, the ohmic electrode 111, the current narrowing layer 112, and the pad electrode 113 are formed. The scribe flaws are formed in a broken-line shape in a portion excluding the ridge Ri by laser scribing or mechanical scribing.

Then, the substrate 101 is cleaved such that the light emission facet 1F and the rear facet 1B are formed. Thus, the substrate 101 is separated into sticks.

Therefore, the separated substrate 101 is introduced into an ECR sputter film formation device.

The light emission facet 1F is irradiated with ECR plasma for five minutes. Note that the plasma is generated under conditions of a microwave power of 500 W in a N₂ gas atmosphere of approximately 0.02 Pa. Thus, the light emission facet 1F is cleaned while being slightly etched. In this case, no RF power (high-frequency power) is applied to a sputter target. Thereafter, the first dielectric multilayer film 210 (see FIG. 2) is formed on the light emission facet 1F by ECR sputtering.

Similarly, the rear facet 1B is irradiated with plasma for five minutes. Thus, the rear facet 1B is cleaned while being slightly etched. In the case, no RF power is applied to a sputter target. Thereafter, the second dielectric multilayer film 220 (see FIG. 2) is formed on the rear facet 1B by ECR sputtering.

Thus cleaning the light emission facet 1F and the rear facet 1B by the ECR plasma inhibits the degradation of the cavity facet and the occurrence of optical breakdown of the cavity facet. This allows the laser characteristics of the nitride based semiconductor laser device 1 to be improved.

Thereafter, the stick-shaped substrate 101 is separated into chips at the center of the groove G formed on the substrate 101. Thus, the nitride based semiconductor laser device 1 shown in FIG. 1 is completed.

2. Second Embodiment

As to a nitride based semiconductor laser device according to a second embodiment, the difference from the nitride based semiconductor laser device 1 according to the first embodiment will be described.

FIG. 5 is a vertical sectional view of the nitride based semiconductor laser device according to the second embodiment. In FIG. 5, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 5 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A first dielectric multilayer film 210 is formed on a light emission facet 1F of the nitride based semiconductor laser device 1. The first dielectric multilayer film 210 has a structure in which an AlO_(X)N_(Y) film (X<Y) 211 a and an Al₂O₃ film 212 a are laminated in this order. Here, the refractive index of the AlO_(X)N_(Y) film 211 a is approximately 1.9. The AlO_(X)N_(Y) film 211 a serving as an oxynitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio functions as a protective film of the light emission facet 1F.

The thicknesses of the AlO_(X)N_(Y) film 211 a and the Al₂O₃ film 212 a are approximately 30 nm and approximately 65 nm, respectively. The reflective index of the first dielectric multilayer film 210 is approximately 8%.

On the other hand, a second dielectric multilayer film 220 is formed on a rear facet 1B of the nitride based semiconductor laser device 1. The second dielectric multilayer film 220 has a structure in which an AlO_(X)N_(Y) film (X>Y) 221 a and a reflective film 222 a are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 221 a is approximately 1.7. The AlO_(X)N_(Y) film 221 a serving as an oxynitride film in which the oxygen composition ratio is higher than the nitrogen composition ratio functions as a protective film of the rear facet 1B.

The thickness of the AlO_(X)N_(Y) film 221 a is approximately 30 nm. The reflective film 222 a has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the second dielectric multilayer film 220 is approximately 95%.

3. Third Embodiment

As to a nitride based semiconductor laser device according to a third embodiment, the difference from the nitride based semiconductor laser device 1 according to the first embodiment will be described.

FIG. 6 is a vertical sectional view of the nitride based semiconductor laser device according to the third embodiment. In FIG. 6, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 6 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A first dielectric multilayer film 210 is formed on a light emission facet 1F of the nitride based semiconductor laser device 1. The first dielectric multilayer film 210 has a structure in which an AlN film 211 b, an AlO_(X)N_(Y) film (X<Y) 212 b, and an Al₂O₃film 213 b are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 211 b is approximately 1.9. The AlN film 211 b serving as a nitride film functions as a protective film of the light emission facet 1F.

The thicknesses of the AlN film 211 b, the AlO_(X)N_(Y) film 212 b, and the Al₂O₃ film 213 a are approximately 10 nm, approximately 30 nm, and approximately 62 nm, respectively. The reflective index of the first dielectric multilayer film 210 is approximately 8%.

On the other hand, a second dielectric multilayer film 220 is formed on a rear facet 1B of the nitride based semiconductor laser device 1. The second dielectric multilayer film 220 has a structure in which an Al₂O₃ film 221 b, an AlO_(X)N_(Y) film (X<Y) 222 b, an Al₂O₃ film 223 b, and a reflective film 224 b are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 222 b is approximately 1.9. The Al₂O₃ film 221 serving as an oxide film functions as a protective film of the rear facet 1B.

The thicknesses of the Al₂O₃ film 221 b, the AlO_(X)N_(Y) film 222 b, and the Al₂O₃ film 223 b are approximately 60 nm, approximately 30 nm, and approximately 60 nm, respectively. The reflective film 224 b has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the second dielectric multilayer film 220 is approximately 95%.

4. Fourth Embodiment

As to a nitride based semiconductor laser device according to a fourth embodiment, the difference from the nitride based semiconductor laser device 1 according to the first embodiment will be described.

FIG. 7 is a vertical sectional view of the nitride based semiconductor laser device according to the fourth embodiment. In FIG. 7, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 7 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A first dielectric multilayer film 210 is formed on a light emission facet 1F of the nitride based semiconductor laser device 1. The first dielectric multilayer film 210 has a structure in which an AlO_(X)N_(Y) film (X<Y) 211 c, an AlO_(X)N_(Y) film (X>Y) 212 c, and an Al₂O₃ film 213 c are laminated in this order. The refractive indexes of the AlO_(X)N_(Y) film 211 c and the AlO_(X)N_(Y)film 212 c are approximately 1.9 and approximately 1.7, respectively. The AlO_(X)N_(Y) film 211 c serving as an oxynitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio functions as a protective film of the light emission facet 1F.

The thicknesses of the AlO_(X)N_(Y) film 211 c, the AlO_(X)N_(Y) film 212 c, and the Al₂O₃ film 213 c are approximately 30 nm, approximately 30 nm, and approximately 35 nm, respectively. The reflective index of the first dielectric multilayer film 210 is approximately 8%.

On the other hand, a second dielectric multilayer film 220 is formed on a rear facet 1B of the nitride based semiconductor laser device 1. The second dielectric multilayer film 220 has a structure in which an AlO_(X)N_(Y) film (X>Y) 221 c, an AlO_(X)N_(Y) film (X<Y) 222 c, and a reflective film 223 c are laminated in this order. The refractive indexes of the AlO_(X)N_(Y) film 221 c and the AlO_(X)N_(Y) film 222 c are approximately 1.7 and approximately 1.9, respectively. The AlO_(X)N_(Y) film 221 in which the oxygen composition ratio is higher than the nitrogen composition ratio functions as a protective film of the rear facet 1B.

The thicknesses of the AlO_(X)N_(Y) film (X>Y) 221 c and the AlO_(X)N_(Y) film (X<Y) 222 c are approximately 30 nm and approximately 30nm, respectively. The reflective film 223 c has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the second dielectric multilayer film 220 is approximately 95%.

5. Correspondences Between Elements in Claims and Parts in Embodiments

In the following two paragraphs, non-limiting examples of correspondences between various elements recited in the claims below and those described above with respect to various preferred embodiments of the present invention are explained.

In the first to fourth embodiments described above, the optical waveguide WG is an example of an optical waveguide extending in a substantial [0001] direction, the light emission facet 1F is an example of one facet composed of a substantial (0001) plane, and the rear facet 1B is an example of the other facet composed of a substantial (000 1) plane.

Furthermore, the light emission facet 1F and the rear facet 1B are examples of a cavity facet, and the nitride based semiconductor layer including the n-type cladding layer 103, the n-type carrier blocking layer 104, the n-type optical guide layer 105, the active layer 106, the p-type optical guide layer 107, the p-type cap layer 108, the p-type cladding layer 109, and the p-type contact layer 110 is an example of a nitride based semiconductor layer.

In the first embodiment, the AlN film 211 is an example of a first protective film including nitrogen as a constituent element, and the Al₂O₃ film 221 is an example of a second protective film including oxygen as a constituent element. In the second embodiment, the AlO_(X)N_(Y) film (X<Y) 211 a is an example of a first protective film including nitrogen as a constituent element, and the AlO_(X)N_(Y) film (X>Y) 221 a is an example of a second protective film including oxygen as a constituent element. In the third embodiment, the AlN film 211 b is an example of a first protective film including nitrogen as a constituent element, and the Al₂O₃ film 221 b is an example of a second protective film including oxygen as a constituent element. In the fourth embodiment, the AlO_(X)N_(Y) film (X<Y) 211 c is an example of a first protective film including nitrogen as a constituent element, and the AlO_(X)N_(Y) film (X>Y) 221 c is an example of a second protective film including oxygen as a constituent element.

In the first embodiment, the AlN 211 and the Al₂O₃ film 212 in the first dielectric multilayer film 210 are respectively examples of a nitride film and an oxide film. In the second embodiment, the AlO_(X)N_(Y) film (X<Y) 211 a and the Al₂O₃ film 212 a in the first dielectric multilayer film 210 are respectively examples of an oxynitride film and an oxide film. In the third embodiment, the AlN film 211 b, the AlO_(X)N_(Y) film (X<Y) 212 b, and the Al₂O₃ film 213 b in the first dielectric multilayer film 210 are respectively examples of a nitride film, an oxynitride film, and an oxide film. In the fourth embodiment, the AlO_(X)N_(Y) film (X<Y) 211 c, the AlO_(X)N_(Y) film (X>Y) 212 c, and the Al₂O₃ film 213 c in the first dielectric multilayer film 210 are respectively examples of a first oxynitride film, a second oxynitride film, and an oxide film.

As each of constituent elements recited in the claims, various other elements having configurations or functions described in the claims can be also used.

6. Effects of First to Fourth Embodiments

(a)

In the nitride based semiconductor laser devices according to the first to fourth embodiments, one facet composed of a substantial (0001) plane and the other facet composed of a substantial (000 1) plane constitute a pair of cavity facets of an optical waveguide extending in a substantial [0001] direction, and laser light is respectively emitted from the one facet and the other facet.

The one facet composed of the substantial (0001) plane is easily covered with a Group 13 element such as gallium because it is a Group 13 element polar plane. Here, the first protective film including nitrogen as a constituent element is provided on the one facet. This prevents a surface state caused by binding of a Group 13 element and oxygen from being generated in the interface between the one facet and the first protective film, thereby preventing a laser light from being absorbed at the surface state in the interface between the one facet and the first protective film.

On the other hand, the other facet composed of the substantial (000 1) plane is easily covered with nitrogen atoms because it is a nitrogen polar plane. Therefore, a surface state caused by binding of a Group 13 element and oxygen is difficult to generate on the other facet. Furthermore, a second protective film including oxygen as a constituent element is provided on the other facet. In a case where the second protective film includes oxygen as a constituent element, absorption of laser light is less, as compared with that in a case where it includes nitrogen as a constituent element. This inhibits laser light from being absorbed by the second protective film.

This allows the luminous efficiency of the laser light to be sufficiently improved.

Furthermore, the intensity of the laser light emitted from the one facet is higher than the intensity of the laser light emitted from the other facet.

In this case, the one facet composed of the substantial (0001) plane is taken as a principal light emission facet. Here, the one facet is chemically stabler, as compared with the other facet composed of the substantial (000 1) plane. This makes it more difficult for the substantial (0001) plane to have recesses and projections formed therein, as compared with the substantial (000 1) plane at the time of manufacturing, thereby making it difficult for the laser light to be scattered on the one facet. Therefore, a preferable far field pattern having few ripples can be efficiently obtained.

Each of a portion of the one facet and a portion of the other facet in the optical waveguide has recesses and projections, and the depth of the recesses in the one facet is smaller than the depth of the recesses in the other facet.

In this case, the laser light is difficult to scatter on the one facet. Therefore, a preferable far field pattern having few ripples can be efficiently obtained from the one facet.

(b) Effect of Protective Film Covering Light Emission Facet 1F and Rear Facet 1B

In the first embodiment, the AlN film 211 covers the light emission facet 1F. That is, the nitride film is formed on the (0001) plane serving as a Ga polar plane. In this case, a surface state caused by binding of a Ga atom and an O atom can be prevented from being generated in the interface between the light emission facet 1F and the AlN film 211. This prevents laser light from being absorbed at the surface state in the interface between the light emission facet 1F and the AlN film 211. Therefore, it is possible to sufficiently improve the luminous efficiency of the laser light.

Furthermore, in the first embodiment, the Al₂O₃ film 221 covers the rear facet 1B. That is, the oxide film is formed on the (000 1) plane serving as an N polar plane. The absorption amount of the laser light by the oxide film is smaller than the absorption amount of the laser light by the nitride film. Furthermore, a surface state is difficult to generate in the interface between the (000 1) plane serving as an N polar plane and the oxide film. Therefore, the oxide film is formed on the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

In the second embodiment, the AlO_(X)N_(Y) film (X<Y) 211 a serving as a nitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio is formed on the light emission facet 1F composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the AlO_(X)N_(Y) film (X>Y) 221 a serving as an oxide film in which the oxygen composition ratio is higher than the nitrogen composition ratio is formed on the rear facet 1B composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

In the third embodiment, the AlN film 211 b serving as a nitride film is formed on the light emission facet 1F composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the Al₂O₃ film 221 b serving as an oxide film is formed on the rear facet 1B composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

In the fourth embodiment, the AlO_(X)N_(Y) film (X<Y) 211 c serving as a nitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio is formed on the light emission facet 1F composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the AlO_(X)N_(Y) film (X>Y) 221 c serving as an oxide film in which the oxygen composition ratio is higher than the nitrogen composition ratio is formed on the rear facet 1B composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

(c) Effect of Taking (0001) Plane as Light Emission Facet 1F

In the present embodiment, the (0001) plane is taken as the light emission facet 1F, so that the depth of the recesses in the light emission facet 1F is smaller than the depth of the recesses in the rear facet 1B. This can inhibit the laser light from being scattered on the light emission facet 1F. As a result, a preferable far field pattern having few ripples can be obtained when the nitride based semiconductor laser device 1 is operated.

Furthermore, the second dielectric multilayer film 220 having a high reflective index is formed on the rear facet 1B. Even if a part of the laser light is scattered by the recesses and projections in the rear facet 1B, therefore, the reduction in the reflection amount is less affected by the scattering. This inhibits a power of the laser light from being reduced.

7. Fifth Embodiment

(1) Configuration of Nitride Based Semiconductor Laser Device

As to a nitride based semiconductor laser device according to a fifth embodiment, the difference from the nitride based semiconductor laser device 1 according to the first embodiment will be described.

FIG. 8 is a vertical sectional view of the nitride based semiconductor laser device according to the fifth embodiment. In FIG. 8, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 8 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

As shown in FIG. 8, a light emission facet 1Fa and a rear facet 1Ba of the nitride based semiconductor laser device 1 are respectively composed of a cleavage plane of (000 1) and a cleavage plane of (0001).

A third dielectric multilayer film 230 is formed on the light emission facet 1Fa. The third dielectric multilayer film 230 has a structure in which an Al₂O₃ film 231, an AlN film 232, and an SiO₂ 233 are laminated in this order. Thus, the Al₂O₃ film 231 serving as an oxide film functions as a protective film of the light emission facet 1Fa.

The thicknesses of the Al₂O₃ film 231, the AlN film 232, and the SiO₂ film 233 are approximately 120 nm, approximately 10 nm, and approximately 95 nm, respectively. The reflective index of the third dielectric multilayer film 230 is approximately 7%.

A fourth dielectric multilayer film 240 is formed on the rear facet 1Ba. The fourth dielectric multilayer film 240 has a structure in which an AlN film 241, a reflective film 242, and an AlN film 243 are laminated in this order. Thus, the AlN film 241 serving as a nitride film functions as a protective film of the rear facet 1Ba.

The respective thicknesses of the AlN films 241 and 243 are 10 nm. The reflective film 242 has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the fourth dielectric multilayer film 240 is approximately 95%.

In the nitride based semiconductor laser device 1 thus formed, a voltage is applied between a pad electrode 113 and an n-side electrode 114, so that laser light is respectively emitted from the light emission facet 1Fa and the rear facet 1Ba.

In the present embodiment, the third dielectric multilayer film 230 having a reflective index of approximately 7% is provided on the light emission facet 1Fa, and the fourth dielectric multilayer film 240 having a reflective index of approximately 95% is provided on the rear facet 1Ba, as described above. This causes the intensity of the laser light emitted from the light emission facet 1Fa to be significantly higher than the intensity of the laser light emitted from the rear facet 1Ba. That is, the light emission facet 1Fa is a principal emission facet of the laser light.

Here, in the present embodiment, undoped In_(0.02)Ga_(0.98)N is used as a barrier layer 106 a in an active layer 106, and undoped In_(0.15)Ga_(0.85)N is used as a well layer 106 b in the active layer 106.

Thus, in the nitride based semiconductor laser device 1 according to the present embodiment, the In composition ratio in the well layer 106 b is 0.15, and is significantly lower than the Ga composition ratio. This sufficiently inhibits recesses and projections of the active layer 106 from becoming significant in each of the light emission facet 1Fa and the rear facet 1Ba.

(2) Method for Manufacturing Nitride Based Semiconductor Laser Device 1

As to a method for manufacturing the nitride based semiconductor laser device 1 having the above-mentioned configuration, the difference from that in the above-mentioned first embodiment will be described.

When the nitride based semiconductor laser device 1 according to the present embodiment is manufactured, a substrate 101 on which an n-type layer 102, an n-type cladding layer 103, an n-type carrier blocking layer 104, an n-type optical guide layer 105, an active layer 106, a p-type optical guide layer 107, a p-type cap layer 108, a p-type cladding layer 109, and a p-type contact layer 110 are formed is cleaved such that a light emission facet 1Fa composed of a (000 1) plane and a rear facet 1Ba composed of a (0001) plane are formed.

Thereafter, a third dielectric multilayer film 230 is formed on the cleaned light emission facet 1Fa by ECR sputtering. Furthermore, a fourth dielectric multilayer film 240 is formed on the cleaned rear facet 1Ba by ECR sputtering.

Thereafter, the stick-shaped substrate 101 is separated into chips at the center of a groove G formed on the substrate 101. Thus, the nitride based semiconductor laser device 1 according to the fifth embodiment shown in FIG. 8 is completed.

8. Sixth Embodiment

As to a nitride based semiconductor laser device according to a sixth embodiment, the difference from the nitride based semiconductor laser device 1 according to the fifth embodiment will be described.

FIG. 9 is a vertical sectional view of the nitride based semiconductor laser device according to the sixth embodiment. In FIG. 9, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 9 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A third dielectric multilayer film 230 is formed on a light emission facet 1Fa. The third dielectric multilayer film 230 has a structure in which an AlO_(X)N_(Y) (X>Y) 231 a and an Al₂O₃ film 232 a are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 231 a is approximately 1.7. The AlO_(X)N_(Y) film 231 a serving as an oxynitride film in which the oxygen composition ratio is higher than the nitrogen composition ratio functions as a protective film of the light emission facet 1Fa.

The thicknesses of the AlO_(X)N_(Y) film 231 a and the Al₂O₃ film 232 a are approximately 30 nm and approximately 57 nm, respectively. The reflective index of the third dielectric multilayer film 230 is approximately 8%.

A fourth dielectric multilayer film 240 is formed on a rear facet 1Ba. The fourth dielectric multilayer film 240 has a structure in which an AlO_(X)N_(Y) (X<Y) 241 a and a reflective film 242 a are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 241 a is approximately 1.9. The AlO_(X)N_(Y) film 241 a serving as an oxynitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio functions as a protective film of the rear facet 1Ba.

The thickness of the AlO_(X)N_(Y) film 241 a is approximately 30 nm. The reflective film 242 a has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the fourth dielectric multilayer film 240 is approximately 95%.

9. Seventh Embodiment

As to a nitride based semiconductor laser device according to a seventh embodiment, the difference from the nitride based semiconductor laser device according to the fifth embodiment will be described.

FIG. 10 is a vertical sectional view of the nitride based semiconductor laser device according to the seventh embodiment. In FIG. 10, a vertical section of the nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 10 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A third dielectric multilayer film 230 is formed on a light emission facet 1Fa. The third dielectric multilayer film 230 has a structure in which an Al₂O₃ film 231 b, an AlO_(X)N_(Y) film (X<Y) 232 b, and an Al₂O₃ film 233 b are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 232 b is approximately 1.9. The Al₂O₃ film 231 b serving as an oxide film functions as a protective film of the light emission facet 1Fa.

The thicknesses of the Al₂O₃ film 231 b, the AlO_(X)N_(Y) film 232 b, and the Al₂O₃ film 233 b are approximately 10 nm, approximately 30 nm, and approximately 52 nm, respectively. The reflective index of the third dielectric multilayer film 230 is approximately 8%.

A fourth dielectric multilayer film 240 is formed on a rear facet 1Ba. The fourth dielectric multilayer film 240 has a structure in which an AlN film 241 b, an AlO_(X)N_(Y) film (X<Y) 242 b, an Al₂O₃ film 243 b, and a reflective film 244 b are laminated in this order. The refractive index of the AlO_(X)N_(Y) film 242 b is approximately 1.9. The AlN film 241 b serving as a nitride film functions as a protective film of the rear facet 1Ba.

The thicknesses of the AlN film 241 b, the AlO_(X)N_(Y) film 242 b, and the Al₂O₃ film 243 b are approximately 10 nm, approximately 30 nm, and approximately 60 nm, respectively. The reflective film 244 b has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the fourth dielectric multilayer film 240 is approximately 95%.

10. Eighth Embodiment

As to a nitride based semiconductor laser device according to an eighth embodiment, the difference from the nitride based semiconductor laser device 1 according to the fifth embodiment will be described.

FIG. 11 is a vertical sectional view of the nitride based semiconductor laser device according to the eighth embodiment. In FIG. 11, a vertical section of a nitride based semiconductor laser device 1 along a [0001] direction is shown, similarly to the vertical section shown in FIG. 2 in the first embodiment. A vertical section taken along a line A2-A2 shown in FIG. 11 is the same as the vertical section of the nitride based semiconductor laser device 1 shown in FIG. 1.

A third dielectric multilayer film 230 is formed on a light emission facet 1Fa. The third dielectric multilayer film 230 has a structure in which an AlO_(X)N_(Y) film (X>Y) 231 c, an AlO_(X)N_(Y)film (X<Y) 232 c, and an Al₂O₃ film 233 c are laminated in this order. The refractive indexes of the AlO_(X)N_(Y) film 231 c and the AlO_(X)N_(Y) film 232 c are approximately 1.7 and approximately 1.9, respectively. The AlO_(X)N_(Y) film (X>Y) 231 c serving as an oxynitride film in which the oxygen composition ratio is higher than the nitrogen composition ratio functions as a protective film of the light emission facet 1Fa.

The thicknesses of the AlO_(X)N_(Y) film 231 c, the AlO_(X)N_(Y) film 232 c, and the Al₂O₃ film 233 c are approximately 30 nm, approximately 30 nm, and approximately 15 nm, respectively. The reflective index of the third dielectric multilayer film 230 is approximately 8%.

A fourth dielectric multilayer film 240 is formed on a rear facet 1Ba. The fourth dielectric multilayer film 240 has a structure in which an AlO_(X)N_(Y) film (X<Y) 241 c, an AlO_(X)N_(Y) film (X>Y) 242 c, and a reflective film 243 c are laminated in this order. The refractive indexes of the AlO_(X)N_(Y) film 241 c and the AlO_(X)N_(Y) film 242 c are approximately 1.9 and approximately 1.7, respectively. The AlO_(X)N_(Y) film 241 c serving as an oxynitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio functions as a protective film of the rear facet 1Ba.

The thicknesses of the AlO_(X)N_(Y) film 241 c and the AlO_(X)N_(Y) film 242 c are approximately 30 nm and approximately 30 nm, respectively. The reflective film 243 c has a ten-layer structure in which five SiO₂ films having a thickness of approximately 70 nm and five TiO₂ films having a thickness of approximately 45 nm are alternately laminated. The SiO₂ film is used as a low refractive index film, and the TiO₂ film is used as a high refractive index film. The reflective index of the fourth dielectric multilayer film 240 is approximately 95%.

11. Correspondences Between Elements in Claims and Parts in Embodiments

In the following two paragraphs, non-limiting examples of correspondences between various elements recited in the claims below and those described above with respect to various preferred embodiments of the present invention are explained.

In the fifth to eighth embodiments described above, the optical waveguide WG is an example of an optical waveguide extending in a substantial [0001] direction, the rear facet 1Ba is an example of one facet composed of a substantial (0001) plane, and the light emission facet 1Fa is an example of the other facet composed of a substantial (000 1) plane.

Furthermore, the light emission facet 1Fa and the rear facet 1Ba are examples of a cavity facet, and the nitride based semiconductor layer including the n-type cladding layer 103, the n-type carrier blocking layer 104, the n-type optical guide layer 105, the active layer 106, the p-type optical guide layer 107, the p-type cap layer 108, the p-type cladding layer 109, and the p-type contact layer 110 is an example of a nitride based semiconductor layer.

In the fifth embodiment, the Al₂O₃ film 231 is an example of a second protective film including oxygen as a constituent element, and the AlN film 241 is an example of a first protective film including nitrogen as a constituent element. In the sixth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 a is an example of a second protective film including oxygen as a constituent element, and the AlO_(X)N_(Y) film (X<Y) 241 a is an example of a first protective film including nitrogen as a constituent element. In the seventh embodiment, the Al₂O₃ film 231 b is an example of a second protective film including oxygen as a constituent element, and the AlN film 241 b is an example of a first protective film including nitrogen as a constituent element. In the eighth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 c is an example of a second protective film including oxygen as a constituent element, and the AlO_(X)N_(Y) film (X<Y) 241 c is an example of a first protective film including nitrogen as a constituent element.

In the fifth embodiment, the Al₂O₃ film 231, the AlN film 232, and the SiO₂ film 233 in the third dielectric multilayer film 230 are respectively examples of a first oxide film, a nitride film, and a second oxide film. In the sixth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 a and the Al₂O₃ film 232 a in the third dielectric multilayer film 230 are respectively examples of an oxynitride film and an oxide film. In the seventh embodiment, the Al₂O₃ film 231 b, the AlO_(X)N_(Y) film (X<Y) 232 b, and the Al₂O₃ film 233 b in the third dielectric multilayer film 230 are respectively examples of a first oxide film, an oxynitride film, and a second oxide film. In the eighth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 c, the AlO_(X)N_(Y) film (X<Y) 232 c, and the Al₂O₃ film 233 c are respectively examples of a first oxynitride film, a second oxynitride film, and an oxide film.

As each of constituent elements recited in the claims, various other elements having configurations or functions described in the claims can be also used.

12. Effects of fifth to eighth embodiments

(a)

In the nitride based semiconductor devices according to the fifth to eighth embodiments, one facet composed of a substantial (0001) plane and the other facet composed of a substantial (000 1) plane constitute a pair of cavity facets of an optical waveguide extending in a substantial [0001] direction, and laser light is respectively emitted from the one facet and the other facet.

The one facet composed of the substantial (0001) plane is easily covered with a Group 13 element such as gallium because it is a Group 13 element polar plane. Here, the first protective film including nitrogen as a constituent element is provided on the one facet. This prevents a surface state caused by binding of a Group 13 element and oxygen from being generated in the interface between the one facet and the first protective film, thereby preventing laser light from being absorbed at the surface state in the interface between the one facet and the first protective film.

On the other hand, the other facet composed of the substantial (0001) plane is easily covered with a nitrogen atom because it is a nitrogen polar plane. Therefore, a surface state caused by binding of a Group 13 element and oxygen is difficult to generate on the other facet. Furthermore, a second protective film including oxygen as a constituent element is provided on the other facet. In a case where the second protective film includes oxygen as a constituent element, absorption of the laser light is less, as compared with that in a case where it includes nitrogen as a constituent element. This inhibits laser light from being absorbed by the second protective film.

This allows the luminous efficiency of the laser light to be sufficiently improved.

Furthermore, the intensity of the laser light emitted from the other facet is higher than the intensity of the laser light emitted from the one facet.

In this case, the other facet composed of the substantial (000 1) plane is taken s a principal light emission facet. Here, the one facet composed of the substantial (0001) plane is easy to oxidize because it is easily covered with a Group 13 element. On the other hand, the other facet composed of the substantial (000 1) plane is difficult to oxidize because it is easily covered with nitrogen atoms. This inhibits the principal light emission facet from being degraded by oxidation, making a stable high power operation feasible.

(b) Effect of Protective Film Covering Light Emission Facet 1Fa and Rear Facet 1Ba

In the fifth embodiment, the Al₂O₃ film 231 covers the light emission facet 1Fa. That is, the oxide film is formed on the (000 1) plane serving as an N polar plane. The absorption amount of the laser light by the oxide film is smaller than the absorption amount of the laser light by the nitride film. Furthermore, a surface state is difficult to generate in the interface between the (000 1) plane and the oxide film. Therefore, the oxide film is formed on the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

Furthermore, in the fifth embodiment, the AlN film 241 covers the rear facet 1Ba. That is, the nitride film is formed on the (0001) plane serving as a Ga polar plane. In this case, a surface state caused by binding of a Ga atom and an O atom is prevented from being generated in the interface between the rear facet 1Ba and the AlN film 241. This prevents laser light from being absorbed at a surface state in the interface between the rear facet 1F and the AlN film 241. Therefore, it is possible to sufficiently improve the luminous efficiency of the laser light.

In the sixth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 a serving as an oxide film in which the oxygen composition ratio is higher than the nitrogen composition ratio is formed on the light emission facet 1Fa composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the AlO_(X)N_(Y) film (X<Y) 241 a serving as a nitride film in which the nitrogen composition ratio is higher than the oxide composition ratio is formed on the rear facet 1Ba composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

In the seventh embodiment, the Al₂O₃ film 231 b serving as an oxide film is formed on the light emission facet 1Fa composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the AlN film 241 b serving as a nitride film is formed on the rear facet 1Ba composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

In the eighth embodiment, the AlO_(X)N_(Y) film (X>Y) 231 c serving as an oxide film in which the oxygen composition ratio is higher than the nitrogen composition ratio is formed on the light emission facet 1Fa composed of the (000 1) plane. This allows the luminous efficiency of the laser light to be sufficiently improved. Furthermore, the AlO_(X)N_(Y) film (X<Y) 241 c serving as a nitride film in which the nitrogen composition ratio is higher than the oxygen composition ratio is formed on the rear facet 1Ba composed of the (0001) plane. This allows the luminous efficiency of the laser light to be sufficiently improved.

(c) Effect of Taking (0001) Plane As Light Emission Facet 1F

The (0001) plane serving as a Ga polar plane is easy to oxidize because its top surface is easily covered with Ga atoms. On the other hand, the (000 1) plane serving as an N polar plane is difficult to oxidize because its top surface is easily covered with N atoms.

In the present embodiment, the (000 1) plane is taken as the light emission facet 1Fa. This inhibits the light emission facet 1Fa from being degraded by oxidation. This allows the laser characteristics of the nitride based semiconductor laser device 1 to be kept stable, making a stable high power operation feasible.

Furthermore, in the present embodiment, undoped In_(0.15)Ga_(0.85)N is used as the well layer 106 b. When the In composition ratio is significantly lower than the Ga composition ratio in the well layer 106 b, the recesses and projections of the active layer 106 in each of the light emission facet 1Fa and the rear facet 1Ba are sufficiently inhibited from becoming significant.

In the (000 1) plane where greater recesses and projections are more easily formed than those in the (0001) plane, the recesses and projections are prevented from becoming significant. As a result, when the scattering of the laser light emitted from the light emission facet 1Fa is reduced, so that a preferable far field pattern having few ripples is obtained.

13. Modified Example of Fifth to Eighth Embodiments

A modified example of the fifth to eighth embodiments will be then described. The following is the difference between the nitride based semiconductor laser device 1 according to the above-mentioned embodiments and the nitride based semiconductor laser device 1 in this example.

Al_(0.03)Ga_(0.97)N is used as the n-type cladding layer 103 and the p-type cladding layer 109 in this example. The amount of doping of Si into the n-type cladding layer 103 and the amount of doping of Mg into the p-type cladding layer 109 are the same as those in the above-mentioned embodiments. Furthermore, the respective carrier concentrations and thicknesses of the n-type cladding layer 103 and the p-type cladding layer 109 are the same as those in the above-mentioned embodiments.

An n-type GaN is used as the n-type optical guide layer 105, n-type Al_(0.10)Ga_(0.90)N is used as the n-type carrier blocking layer 104, and n-type In_(0.05)Ga_(0.95)N is used as the n-type optical guide layer 105. The respective amounts of doping of Mg into the n-type carrier blocking layer 104 and the n-type optical guide layer 105 are the same as those in the second embodiment. Furthermore, the respective carrier concentrations and thicknesses of the n-type carrier blocking layer 104 and the n-type optical guide layer 105 are the same as those in the above-mentioned embodiments.

An active layer 106 having an MQW structure in which three barrier layers 106 a composed of undoped In_(0.25)Ga_(0.75)N and two well layers 106 b composed of undoped In_(0.55)Ga_(0.45)N are alternately laminated is used in this example. The respective thicknesses of each of the barrier layers 106 a and each of the well layers 106 b are the same as those in the above-mentioned embodiments.

P-type Al_(0.10)Ga_(0.90)N is used as the p-type cap layer 108 in this example. The respective amounts of doping of Mg into the p-type optical guide layer 107 and the p-type cap layer 108 are the same as those in the second embodiment. Furthermore, the respective carrier concentrations and thicknesses of the p-type optical guide layer 107 and the p-type cap layer 108 are the same as those in the above-mentioned embodiments.

In this example, the In composition ratio included in the active layer 106 is higher than the Ga composition ratio included therein. In this case, a portion of the active layer 106 in the light emission facet 1Fa is easier to oxidize. Therefore, taking the (000 1) plane that is difficult to oxidize as the light emission facet 1Fa can inhibit the light emission facet 1Fa from being degraded by oxidation. This allows the laser characteristics of the nitride based semiconductor laser device 1 to be kept stable, making a stable high power operation feasible.

14. Other Embodiments

(1) Although in the above-mentioned embodiments, the oxide films in the first to fourth dielectric multilayer films 210, 220, 230, 240 are formed of Al₂O₃, the nitride film is formed of AlN, and the oxynitride film is formed of AlO_(X)N_(Y), the present invention is not limited to the same. The oxide films in the first to fourth dielectric multilayer films 210, 220, 230, and 240 may be formed of one or more of Al₂O₃, SiO₂, ZrO₂, Ta₂O₅, HfO₂, and AlSiO_(X), for example. Here, X is a real number larger than zero. The nitride films in the first to fourth dielectric multilayer films 210, 220, 230, and 240 may be formed of one or both of AlN and Si₃N₄, for example. Furthermore, the oxynitride film may be formed of one or more of AlO_(X)N_(Y), SiO_(X)N_(Y), and TaO_(X)N_(Y) for example. Here, X and Y are real numbers larger than zero.

In the above-mentioned embodiments, the ratio of the nitrogen composition ratio to the oxygen composition ratio in each of the AlO_(X)N_(Y) film (X<Y) 211 a, 212 b, 222 b, 221 c, 222 c, 241 a, 232 b, 242 b, 232 c, and 241 c is 54(%):46(%), for example.

Although in the above-mentioned embodiments, SiO₂ is used as a material for a low refractive index film, and TiO₂ is used as a material for a high refractive index film. Another material such as MgF₂or Al₂O₃may be used as a material for a low refractive index film. Another material such as ZrO₂, Ta₂O₅, CeO₂, Y₂O₃, Nb₂O₅, or HfO₂ may be used as a material for a high refractive index film.

(2) When at least one of the light emission facet 1F and the rear facet 1B or at least one of the light emission facet 1Fa and the rear facet 1Ba is formed by cleavage, a main surface of the active layer 106 may have any plane direction in a range of ± approximately 0.3 degrees from a (H, K, −H−K, 0) plane. Note that H and K are any integers, and at least one of H and K is an integer other than zero. Furthermore, the light emission facets 1F and 1Fa and the rear facets 1B and 1Ba that are formed by cleavage may respectively have any plane directions in a range of ± approximately 0.3 degrees from the (0001) plane and the (000 1) plane.

When the light emission facets 1F and 1Fa and the rear facets 1B and 1Ba are formed by methods other than cleavage, for example, etching, grinding, or selective growth, the light emission facets 1F and 1Fa and the rear facets 1B and 1Ba may respectively have any plane directions in a range of ± approximately 25 degrees from the (0001) plane and the (000 1) plane. However, it is desired that the light emission facets 1F and 1Fa and the rear facets 1B and 1Ba are substantially perpendicular (90 degrees ± approximately 5 degrees) to the main surface of the active layer 106.

(3) A nitride of a Group 13 element including at least one of Ga, Al, In, Tl, and B can be used for the substrate 102, the n-type layer 102, the n-type cladding layer 103, the n-type carrier blocking layer 104, the n-type optical guide layer 105, the active layer 106, the p-type optical guide layer 107, the p-type cap layer 108, the p-type cladding layer 109, and the p-type contact layer 110. Specifically, a nitride based semiconductor composed of AlN, InN, BN, TlN, GaN, AlGaN, InGaN, InAlGa or their mixed crystals can be used as a material for each of the layers.

(4) In the first, third, fifth and seventh embodiments, when an AlN film is formed on the one facet (0001), as the protection film of the first layer being in contact with the semiconductor, the AlN film may be formed to have high orientation in the (0001) direction. In this case, thermal conductivity in the (0001) direction becomes increased, and a temperature rise at the semiconductor interface can be suppressed, resulting in improved reliability.

When a second AlN film is further formed as a layer other than the protection film of the first layer as the fifth embodiment, the orientation of the AlN film of the first layer need not necessarily coincide with that of the second AlN film, and the second AlN film need not necessarily be formed to have high orientation as with the AlN film of the first layer.

While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims. 

1. A nitride based semiconductor laser device comprising: a nitride based semiconductor layer having an optical waveguide extending in a substantial [0001] direction and having one facet composed of a substantial (0001) plane and the other facet composed of a substantial (000 1) plane as a pair of cavity facets; a first protective film provided on said one facet and including nitrogen as a constituent element; and a dielectric multilayer film including a second protective film provided on said other facet and including oxygen as a constituent element, wherein the intensity of laser light emitted from said one facet is higher than the intensity of laser light emitted from said other facet, and said dielectric multilayer film includes a first oxide film, an oxynitride film, and a second oxide film that are laminated in this order from said other facet, the nitrogen composition ratio is higher than the oxygen composition ratio in said oxnitride film, and said second protective film is said first oxide film.
 2. The nitride based semiconductor laser device according to claim 1, wherein said first protective film includes no oxygen as a constituent element.
 3. The nitride based semiconductor laser device according to claim 1, wherein said second protective film includes no nitrogen as a constituent element.
 4. The nitride based semiconductor laser device according to claim 1, further comprising a dielectric multilayer film formed on said one facet and including said first protective film, wherein said dielectric multilayer film includes a nitride film, an oxynitride film, and an oxide film that are laminated in this order from said one facet, the nitrogen composition ratio is higher than the oxygen composition ratio in said oxynitride film, and said first protective film is said nitride film.
 5. The nitride based semiconductor laser device according to claim 2, wherein said first protective film includes at least one of AIN and Si₃N₄.
 6. The nitride based semiconductor laser device according to claim 3, wherein said second protective film includes at least one of Al₂O₃, SiO₂, ZrO₂, Ta₂O₅, HfO₂, and AlSiO_(x), where X is a real number larger than zero.
 7. The nitride based semiconductor laser device according to claim 1, wherein said oxynitride film constituting said dielectric multilayer film including said second protective film includes an AlO_(x)N_(y) film where x and y are real numbers larger than zero.
 8. The nitride based semiconductor laser device according to claim 1, wherein said dielectric multilayer film including said second protective film further includes a reflective film laminated on said second oxide film, and said reflective film has a structure that an SiO₂ film and a TiO₂ film are alternately laminated.
 9. The nitride based semiconductor laser device according to claim 4, wherein said oxynitride film constituting said dielectric multilayer film including said first protective film includes an AlO_(x)N_(y) film where x and y are real numbers larger than zero.
 10. The nitride based semiconductor laser device according to claim 4, wherein said nitride film constituting said dielectric multilayer film including said first protective film has orientation in a substantial [0001] direction.
 11. A nitride based semiconductor laser device comprising: a nitride based semiconductor layer having an optical waveguide extending in a substantial [0001] direction and having one facet composed of a substantial (0001) plane and the other facet composed of a substantial (000-1) plane as a pair of cavity facets; a dielectric multilayer film including a first protective film provided on said one facet and including nitrogen as a constituent element; and a second protective film provided on said other facet and including oxygen as a constituent element, wherein the intensity of laser light emitted from said one facet is higher than the intensity of laser light emitted from said other facet, said first protective film includes no oxygen as a constituent element, said dielectric multilayer film includes a nitride film, an oxynitride film, and an oxide film that are laminated in this order from said one facet, the nitrogen composition ratio is higher than the oxygen composition ratio in said oxynitride film, and said first protective film is said nitride film.
 12. The nitride based semiconductor laser device according to claim 11, wherein said second protective film includes no nitrogen as a constituent element.
 13. The nitride based semiconductor laser device according to claim 11, further comprising a dielectric multilayer film formed on said other facet and including said second protective film, wherein said dielectric multilayer film includes a first oxide film, an oxynitride film, and a second oxide film that are laminated in this order from said other facet, the nitrogen composition ratio is higher than the oxygen composition ratio in said oxynitride film, and said second protective film is said first oxide film.
 14. The nitride based semiconductor laser device according to claim 11, wherein said first protective film includes at least one of AlN and Si₃N₄.
 15. The nitride based semiconductor laser device according to claim 12, wherein said second protective film includes at least one of Al₂O₃, SiO₂, ZrO₂, Ta₂O₅, HfO₂, and AlSiO_(x), where X is a real number larger than zero.
 16. The nitride based semiconductor laser device according to claim 13, wherein said oxynitride film constituting said dielectric multilayer film including said second protective film includes an AlO_(x)N_(y) film where x and y are real numbers larger than zero.
 17. The nitride based semiconductor laser device according to claim 13, wherein said dielectric multilayer film including said second protective film further includes a reflective film laminated on said second oxide film, and said reflective film has a structure that an SiO₂ film and a TiO₂ film are alternately laminated.
 18. The nitride based semiconductor laser device according to claim 11, wherein said oxynitride film constituting said dielectric multilayer film including said first protective film includes an AlO_(x)N_(y) film where x and y are real numbers larger than zero.
 19. The nitride based semiconductor laser device according to claim 11, wherein said nitride film constituting said dielectric multilayer film including said first protective film has orientation in a substantial [0001] direction. 